Li, H.*; Liu, Y.*; Zhao, W.*; Liu, B.*; Tominaga, Aki; Shobu, Takahisa; Wei, D.*
International Journal of Plasticity, 165, p.103612_1 - 103612_20, 2023/06
Times Cited Count:3 Percentile:74.38(Engineering, Mechanical)In order to clarify the strength properties of Co-free maraging steel, tensile experiment using high energy synchrotron X-ray diffraction was performed. Diffraction profiles from the martensitic and austenitic phases were obtained, and their strength and width were observed to vary as loading. Analysis of the diffraction profiles showed that the content of martensite in the as-aged material decreased slowly at low stress levels and decreased rapidly at high stress levels. On the other hand, the austenite phase in the as-solution materials was significantly transformed the martensite phase as the stress increased. It was clarified to be responsible for their respective strength properties.